沙伯基礎創新PC LEXAN BPL1000 特性：無鹵阻燃(0.8mm V0)，良好的抗沖擊性，高流動性(25g/10 min)，薄壁應用的理想選擇，用于手機電池外殼
我公司提供的產品均為正牌塑膠原料，品質保證，貨源穩定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權威資料請致電13268582149
PC BPL1000 物性表：
| Physical |
Nominal Value |
Unit |
Test Method |
| Specific Gravity |
1.17 |
g/cm³ |
ASTM D792 |
| Density |
1.20 |
g/cm³ |
ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) |
25 |
g/10 min |
ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) |
23.2 |
cm³/10min |
ISO 1133 |
| Molding Shrinkage - Flow |
|
|
Internal Method |
| -- 2 |
0.50 to 0.70 |
% |
|
| 3.20 mm |
0.50 to 0.70 |
% |
|
| Molding Shrinkage - Across Flow (3.20 mm) |
0.50 to 0.70 |
% |
Internal Method |
| Water Absorption (Saturation, 23°C) |
0.35 |
% |
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
0.15 |
% |
ISO 62 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
| Tensile Modulus 3 |
2680 |
MPa |
ASTM D638 |
| Tensile Modulus |
2460 |
MPa |
ISO 527-2/1 |
| Tensile Strength 4 (Yield) |
63.4 |
MPa |
ASTM D638 |
| Tensile Stress (Yield) |
64.8 |
MPa |
ISO 527-2/50 |
| Tensile Strength 4 (Break) |
51.0 |
MPa |
ASTM D638 |
| Tensile Stress (Break) |
53.5 |
MPa |
ISO 527-2/50 |
| Tensile Elongation 4 (Yield) |
4.8 |
% |
ASTM D638 |
| Tensile Strain (Yield) |
4.7 |
% |
ISO 527-2/50 |
| Tensile Elongation 4 (Break) |
96 |
% |
ASTM D638 |
| Tensile Strain (Break) |
97 |
% |
ISO 527-2/50 |
| Flexural Modulus 5 (50.0 mm Span) |
2670 |
MPa |
ASTM D790 |
| Flexural Modulus 6 |
2370 |
MPa |
ISO 178 |
| Flexural Strength 6, 7 |
94.8 |
MPa |
ISO 178 |
| Flexural Strength 5 (Yield, 50.0 mm Span) |
102 |
MPa |
ASTM D790 |
| Impact |
Nominal Value |
Unit |
Test Method |
| Charpy Notched Impact Strength 8 (23°C) |
18 |
kJ/m² |
ISO 179/1eA |
| Notched Izod Impact (23°C) |
600 |
J/m |
ASTM D256 |
| Notched Izod Impact Strength 9 |
|
|
ISO 180/1A |
| -30°C |
12 |
kJ/m² |
|
| 23°C |
18 |
kJ/m² |
|
| Instrumented Dart Impact (23°C, Total Energy) |
48.6 |
J |
ASTM D3763 |
| Thermal |
Nominal Value |
Unit |
Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) |
106 |
°C |
ASTM D648 |
| Heat Deflection Temperature 10 (1.8 MPa, Unannealed, 64.0 mm Span) |
96.1 |
°C |
ISO 75-2/Af |
| Vicat Softening Temperature |
111 |
°C |
ASTM D1525 11 |
| Vicat Softening Temperature |
|
|
|
| -- |
113 |
°C |
ISO 306/B50 |
| -- |
114 |
°C |
ISO 306/B120 |
| Ball Pressure Test (75°C) |
Pass |
|
IEC 60695-10-2 |
| CLTE - Flow (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ASTM E831 |
| CLTE - Flow (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ISO 11359-2 |
| CLTE - Transverse (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ASTM E831 |
| CLTE - Transverse (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ISO 11359-2 |
| Electrical |
Nominal Value |
Unit |
Test Method |
| Surface Resistivity |
> 1.0E+15 |
ohm |
IEC 60093 |
| Volume Resistivity |
> 1.0E+15 |
ohm·cm |
IEC 60093 |
| Dielectric Strength (1.60 mm, in Oil) |
27 |
kV/mm |
ASTM D149 |
| Relative Permittivity |
|
|
IEC 60250 |
| 50 Hz |
3.00 |
|
|
| 60 Hz |
3.00 |
|
|
| 1 MHz |
2.90 |
|
|
| Dissipation Factor |
|
|
IEC 60250 |
| 50 Hz |
0.030 |
|
|
| 60 Hz |
0.030 |
|
|
| 1 MHz |
0.010 |
|
|
| Comparative Tracking Index |
200 |
V |
IEC 60112 |
| Flammability |
Nominal Value |
Unit |
Test Method |
| Flame Rating - UL |
|
|
UL 94 |
| 0.800 mm |
V-0 |
|
|
| 0.450 mm |
V-2 |
|
|